Abstract:
Deep space missions require self-deployable structures built of ultra-thin materials which can
be carried to space in a limited space. Therefore, a growing demand for ultra-thin woven
composites has been identified in space engineering applications. Understanding their
mechanical behaviour is crucial for the effective optimisation of future structures because they
experience extreme curvatures when in use in both folding and deploying mechanisms. It is
more challenging to predict the overall mechanical behaviour of these composites due to their
complicated geometry and nonlinear behaviour of its constituent parts. A common method to
solve this problem is multiscale modelling, in which the system is simultaneously described by
multiple models at varying scales. Micromechanical, mesomechanical and macromechanical
scales are taken into consideration for woven fibre composites.
Physical experiments revealed that ultra-thin woven fibre composites show a significant drop
in bending stiffness at higher curvatures. The first objective of the study focuses on checking
whether there is a thickness reduction of the plies at high curvatures which can be a possible
reason for the reduced bending stiffness at high curvatures. As the second objective, it is
expected to introduce air voids in resin to capture the non-linear bending response of woven
fibre composites observed under high curvatures.
Due to the deformation of the fibres and the weave structure at higher curvatures, woven fibre
composites may exhibit variations in thickness. Resin matrices usually have lower stiffness
compared to the reinforcing fibres. As a result, when the composite is subjected to higher
curvatures, the fibres on the inner side of the curve may experience compression, leading to a
reduction in thickness, while the resin matrix tends to flow and redistribute in response to the
applied forces. The flow of resin can have both positive and negative effects on the thickness
variation. On one hand, the ability of the resin to flow and redistribute can help accommodate
the compression of the fibres and reduce the overall thickness reduction.
According to the obtained results from the Dry Fibre model and the Resin model, except for
the mid-section of the Dry Fibre model, there is no significant thickness variation at other
locations compared to the original thickness in both the Resin model and Dry Fibre model.
Although there is a thickness reduction at the mid-section of the dry fibre model, at high
curvatures thickness starts to increase again which is against the experimentally observed
bending behaviour. So, according to the obtained thickness variation results from the two
models, there is no clear connection between bending stiffness reduction and thickness
variation.
To check the effect because of voids, Fibre Volume Fraction of the composite was used. The
Fibre Volume Fraction is defined as the ratio of the volume of fibres present to the total volume
of the layer. From the second objective, it was observed that there is a 6-8 % reduction in
longitudinal stiffness, transverse stiffness, and shear stiffness with the void ratio. Variation in
the Poisson’s ratio with the void ratio is low compared to other mechanical properties.